5005 Aluminum Coil Stock – Composite Sheet Material
Commonly used in decorative and architectural applications
5005 aluminium alloy is an aluminium alloy with good resistance to atmospheric corrosion. It is used in decorative and architectural applications. It is a member of the 5000 series of aluminum-magnesium wrought alloys. As such, it is not used in casting. It can attain moderate to high strength by cold working, and has relatively high welded strength, workability, and corrosion resistance compared to other aluminum alloy families. Where anodizing is needed, 5005 is specified for applications similar to 1100 and 3003.
MECHANICAL PROPERTY LIMITS
| Temper | Specified Thickness(in) | Tensile Strength – KSI | Elongationin 2 inches % | |||
|---|---|---|---|---|---|---|
| Ultimate | Yield | |||||
| Min | Max | Min | Max | |||
| H12 | 0.017 – 0.019 | 18 | 24 | – | – | 2 |
| H12 | 0.020 – 0.031 | 18 | 24 | – | – | 3 |
| H12 | 0.032 – 0.050 | 18 | 24 | – | – | 4 |
| H12 | 0.051 – 0.113 | 18 | 24 | – | – | 6 |
| H12 | 0.114 – 0.161 | 18 | 24 | – | – | 7 |
| H12 | 0.162 – 0.250 | 18 | 24 | – | – | 8 |
| H14 | 0.009 – 0.031 | 21 | 27 | – | – | 1 |
| H14 | 0.032 – 0.050 | 21 | 27 | – | – | 2 |
| H14 | 0.051 – 0.113 | 21 | 27 | – | – | 3 |
| H14 | 0.114 – 0.161 | 21 | 27 | – | – | 5 |
| H14 | 0.162 – 0.250 | 21 | 27 | – | – | 6 |
| H16 | 0.006 – 0.031 | 24 | 30 | – | – | 1 |
| H16 | 0.032 – 0.050 | 24 | 30 | – | – | 2 |
| H16 | 0.051 – 0.162 | 24 | 30 | – | – | 3 |
| H18 | 0.006 – 0.031 | 27 | – | – | – | 1 |
| H18 | 0.032 – 0.050 | 27 | – | – | – | 1 |
| H18 | 0.051 – 0.128 | 27 | – | – | – | 3 |
| H32 | 0.017 – 0.019 | 17 | 23 | – | – | 3 |
| H32 | 0.020 – 0.031 | 17 | 23 | – | – | 4 |
| H32 | 0.032 – 0.050 | 17 | 23 | – | – | 5 |
| H32 | 0.051 – 0.113 | 17 | 23 | – | – | 7 |
| H32 | 0.114 – 0.161 | 17 | 23 | – | – | 8 |
| H32 | 0.162 – 0.250 | 17 | 23 | – | – | 9 |
| H34 | 0.009 – 0.012 | 20 | 26 | – | – | 2 |
| H34 | 0.013 – 0.031 | 20 | 26 | – | – | 3 |
| H34 | 0.032 – 0.050 | 20 | 26 | – | – | 4 |
| H34 | 0.051 – 0.113 | 20 | 26 | – | – | 5 |
| H34 | 0.114 – 0.161 | 20 | 26 | – | – | 6 |
| H34 | 0.162 – 0.250 | 20 | 26 | – | – | 7 |
| H36 | 0.006 – 0.007 | 23 | 29 | – | – | 1 |
| H36 | 0.008 – 0.019 | 23 | 29 | – | – | 2 |
| H36 | 0.020 – 0.031 | 23 | 29 | – | – | 3 |
| H36 | 0.032 – 0.162 | 23 | 29 | – | – | 4 |
| H38 | 0.006 – 0.012 | 26 | – | – | – | 1 |
| H38 | 0.013 – 0.019 | 26 | – | – | – | 2 |
| H38 | 0.020 – 0.031 | 26 | – | – | – | 3 |
| H38 | 0.032 – 0.128 | 26 | – | – | – | 4 |
| H39 | 0.006 – 0.063 | 28 | – | – | – | 1 |
| O | 0.006 – 0.007 | 15 | 21 | – | – | 12 |
| O | 0.008 – 0.012 | 15 | 21 | – | – | 14 |
| O | 0.013 – 0.019 | 15 | 21 | – | – | 16 |
| O | 0.020 – 0.031 | 15 | 21 | – | – | 18 |
| O | 0.032 – 0.050 | 15 | 21 | – | – | 20 |
| O | 0.051 – 0.113 | 15 | 21 | – | – | 21 |
| O | 0.114 – 0.249 | 15 | 21 | – | – | 22 |
CHEMICAL COMPOSITION LIMITS (%)
| Si Silicon | Fe Iron | Cu Copper | Mn Manganese | Mg Magnesium | Cr Chromium | Ni Nickel | Zn Zinc | Ti Titanium | Others Each | Total | Total Aluminum Min |
|---|---|---|---|---|---|---|---|---|---|---|---|
| 0.3 | 0.7 | 0.2 | 0.2 | 0.5 – 1.1 | 0.1 | – | 0.25 | 0.10 | 0.05 | 0.15 | Remainder |
- Chemical composition is percent maximum unless shown as a range or a minimum.
- Source: Aluminum Standards and Data – The Aluminum Association, Inc.
- Information presented as a guide for reference purposes only and is not intended to be used for product design or application.
- Aluminum Association
wikipedia.org
ALUMINUM SLITTING CAPABILITIES
GAUGE RANGE
.004″ to .190″ (.102 mm to 4.826 mm)
WIDTH RANGE
.250″ to 60″ (6.365 mm to 1524 mm)
ID
8, 12, 16 or 20 (inches)
OD
78″ maximum
COIL WEIGHT
40,000 lbs maximum
CUT-TO-LENGTH CAPABILITIES
GAUGE RANGE
.015 to .060 (.381 mm to 1.524 mm)
WIDTH RANGE
8” – 48” (203 mm to 1.219 mm)
LENGTH RANGE
12” to 144” (305 mm to 3.658 mm)